| 性能項目 | 測試條件 | 測試方法 | 數(shù)值/描述 | 單位 | |
| 機械性能 | 拉伸強度(引張強度) | ASTM D638/ISO 527 | 130 | kg/cm2(MPa)[Lb/in2] | |
| 斷裂伸長率 | ASTM D638/ISO 527 | % | |||
| 拉伸模量 | ASTM D638/ISO 527 | 18500 | kg/cm2(MPa)[Lb/in2] | ||
| 拉伸屈服伸長率(延伸率) | ASTM D638/ISO 527 | % | |||
| 拉伸斷裂伸長率(延伸率) | ASTM D638/ISO 527 | % | |||
| 彎曲模量(彎曲彈性率) | ASTM D790/ISO 178 | 17500 | kg/cm2(MPa)[Lb/in2] | ||
| 彎曲強度 | ASTM D790/ISO 178 | 200 | kg/cm2(MPa)[Lb/in2] | ||
| 洛氏硬度 | ASTM D785 | ||||
| IZOD 缺口沖擊強度 | 1/4" 23℃ | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | ||
| 1/4" -30℃ | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | |||
| 1/8" 23℃ | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | |||
| 1/8" -30℃ | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | |||
| Charpy沖擊強度 | 23℃ （缺口） | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | ||
| -30℃（缺口） | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | |||
| 23℃（無缺口） | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | |||
| -30℃（無缺口） | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | |||
| 物性性能 | 比重（密度） | ASTM D792/ISO 1183 | 1.96 | ||
| 成型收縮率 | ASTM D955 | % | |||
| 熔融指數(shù)（流動系數(shù)） | 200℃/5kg | ASTM D1238/ISO 1133 | g/10min | ||
| 220℃/10kg | ASTM D1238/ISO 1133 | g/10min | |||
| 吸水率 23℃/24H | ASTM D570/ISO 62 |
%
|
|||
PPS稱聚亞基硫醚，英文名稱:Phenylenesulfide
密度：1.36g/cm3，熔點：250-315度，分解溫度大于480度，長期使用溫度：220-240℃，熱變溫：250-260℃
成型收縮率?。s0.2-0.3%），吸水率低（約0.02%）
注塑料成型條件：
1、預干燥：干燥應在鼓風條件下進行，干燥：130℃～140℃，3-4小時，料層厚度為3公分。
2、注塑溫度：290-330℃范圍之間
3、注射壓力：40-120MPa4、注塑速度：采用中速為宜。
4、模溫： 130-150℃ 主流道錐度應大，流道應短。