VALOX ? Resin 430,451E,4521,457,
VALOX ? Resin 430
SI
| British
| Metric
| PDF
Asia Pacific: COMMERCIAL
33 % glass reinforced, impact modified. Connectors, etc.
Property
TYPICAL PROPERTIES (1)
MECHANICAL
Value
Unit
Standard
Tensile Stress, brk, Type I, 5 mm/min
1080
kgf/cm2
ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min
3.1
%
ASTM D 638
Tensile Modulus, 5 mm/min
88300
kgf/cm2
ASTM D 638
Flexural Stress, brk, 1.3 mm/min, 50 mm span
1770
kgf/cm2
ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span
79600
kgf/cm2
ASTM D 790
Hardness, Rockwell R
125
-
ASTM D 785
IMPACT
Value
Unit
Standard
Izod Impact, unnotched, 23°C
87
cm-kgf/cm
ASTM D 4812
Izod Impact, notched, 23°C
13
cm-kgf/cm
ASTM D 256
THERMAL
Value
Unit
Standard
HDT, 0.45 MPa, 6.4 mm, unannealed
223
°C
ASTM D 648
HDT, 1.82 MPa, 6.4 mm, unannealed
208
°C
ASTM D 648
Relative Temp Index, Elec
130
°C
UL 746B
Relative Temp Index, Mech w/impact
130
°C
UL 746B
Relative Temp Index, Mech w/o impact
140
°C
UL 746B
PHYSICAL
Value
Unit
Standard
Specific Gravity
1.52
-
ASTM D 792
Specific Volume
0.65
cm3/g
ASTM D 792
Water Absorption, 24 hours
0.05
%
ASTM D 570
Mold Shrinkage, flow, 3.2 mm (5)
0.5
%
SABIC Method
Mold Shrinkage, flow, 1.5-3.2 mm (5)
0.3 - 0.5
%
SABIC Method
Mold Shrinkage, flow, 3.2-4.6 mm (5)
0.5 - 0.8
%
SABIC Method
Mold Shrinkage, xflow, 1.5-3.2 mm (5)
0.4 - 0.6
%
SABIC Method
Mold Shrinkage, xflow, 3.2-4.6 mm (5)
0.6 - 0.9
%
SABIC Method
Melt Flow Rate, 250°C/2.16 kgf
11.7
g/10 min
ASTM D 1238
ELECTRICAL
Value
Unit
Standard
Arc Resistance, Tungsten {PLC}
5
PLC Code
ASTM D 495
Hot Wire Ignition {PLC)
0
PLC Code
UL 746A
High Voltage Arc Track Rate {PLC}
0
PLC Code
UL 746A
High Ampere Arc Ign, surface {PLC}
2
PLC Code
UL 746A
Comparative Tracking Index (UL) {PLC}
1
PLC Code
UL 746A
FLAME CHARACTERISTICS
Value
Unit
Standard
UL Recognized, 94HB Flame Class Rating (3)
1.47
mm
UL 94
Source GMD, last updated:2009/03/09
Processing
Parameter
Injection Molding
Value
Unit
Drying Temperature
120
°C
Drying Time
3 - 4
hrs
Drying Time (Cumulative)
12
hrs
Maximum Moisture Content
0.02
%
Melt Temperature
250 - 265
°C
Nozzle Temperature
245 - 260
°C
Front - Zone 3 Temperature
250 - 265
°C
Middle - Zone 2 Temperature
245 - 260
°C
Rear - Zone 1 Temperature
240 - 255
°C
Mold Temperature
65 - 90
°C
Back Pressure
0.3 - 0.7
MPa
Screw Speed
50 - 80
rpm
Shot to Cylinder Size
40 - 80
%
Vent Depth
0.025 - 0.038
mm
Source GMD, last updated:2009/03/09
VALOX ? Resin 430 |
SI | | British | | Metric | Asia Pacific: COMMERCIAL |
| 33 % glass reinforced, impact modified. Connectors, etc. |
|
Property |
| TYPICAL PROPERTIES (1) | ||||
| MECHANICAL | Value | Unit | Standard | |
| Tensile Stress, brk, Type I, 5 mm/min | 1080 | kgf/cm2 | ASTM D 638 | |
| Tensile Strain, brk, Type I, 5 mm/min | 3.1 | % | ASTM D 638 | |
| Tensile Modulus, 5 mm/min | 88300 | kgf/cm2 | ASTM D 638 | |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 1770 | kgf/cm2 | ASTM D 790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 79600 | kgf/cm2 | ASTM D 790 | |
| Hardness, Rockwell R | 125 | - | ASTM D 785 | |
| IMPACT | Value | Unit | Standard | |
| Izod Impact, unnotched, 23°C | 87 | cm-kgf/cm | ASTM D 4812 | |
| Izod Impact, notched, 23°C | 13 | cm-kgf/cm | ASTM D 256 | |
| THERMAL | Value | Unit | Standard | |
| HDT, 0.45 MPa, 6.4 mm, unannealed | 223 | °C | ASTM D 648 | |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 208 | °C | ASTM D 648 | |
| Relative Temp Index, Elec | 130 | °C | UL 746B | |
| Relative Temp Index, Mech w/impact | 130 | °C | UL 746B | |
| Relative Temp Index, Mech w/o impact | 140 | °C | UL 746B | |
| PHYSICAL | Value | Unit | Standard | |
| Specific Gravity | 1.52 | - | ASTM D 792 | |
| Specific Volume | 0.65 | cm3/g | ASTM D 792 | |
| Water Absorption, 24 hours | 0.05 | % | ASTM D 570 | |
| Mold Shrinkage, flow, 3.2 mm (5) | 0.5 | % | SABIC Method | |
| Mold Shrinkage, flow, 1.5-3.2 mm (5) | 0.3 - 0.5 | % | SABIC Method | |
| Mold Shrinkage, flow, 3.2-4.6 mm (5) | 0.5 - 0.8 | % | SABIC Method | |
| Mold Shrinkage, xflow, 1.5-3.2 mm (5) | 0.4 - 0.6 | % | SABIC Method | |
| Mold Shrinkage, xflow, 3.2-4.6 mm (5) | 0.6 - 0.9 | % | SABIC Method | |
| Melt Flow Rate, 250°C/2.16 kgf | 11.7 | g/10 min | ASTM D 1238 | |
| ELECTRICAL | Value | Unit | Standard | |
| Arc Resistance, Tungsten {PLC} | 5 | PLC Code | ASTM D 495 | |
| Hot Wire Ignition {PLC) | 0 | PLC Code | UL 746A | |
| High Voltage Arc Track Rate {PLC} | 0 | PLC Code | UL 746A | |
| High Ampere Arc Ign, surface {PLC} | 2 | PLC Code | UL 746A | |
| Comparative Tracking Index (UL) {PLC} | 1 | PLC Code | UL 746A | |
| FLAME CHARACTERISTICS | Value | Unit | Standard | |
| UL Recognized, 94HB Flame Class Rating (3) | 1.47 | mm | UL 94 | |
| Source GMD, last updated:2009/03/09 |
|
Processing |
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 | °C |
| Drying Time | 3 - 4 | hrs |
| Drying Time (Cumulative) | 12 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 250 - 265 | °C |
| Nozzle Temperature | 245 - 260 | °C |
| Front - Zone 3 Temperature | 250 - 265 | °C |
| Middle - Zone 2 Temperature | 245 - 260 | °C |
| Rear - Zone 1 Temperature | 240 - 255 | °C |
| Mold Temperature | 65 - 90 | °C |
| Back Pressure | 0.3 - 0.7 | MPa |
| Screw Speed | 50 - 80 | rpm |
| Shot to Cylinder Size | 40 - 80 | % |
| Vent Depth | 0.025 - 0.038 | mm |
|
Source GMD, last updated:2009/03/09 |